DATA SHEET KAST-O-LITE 26 LI C/G

DESCRIPTION:

A high performance mix designed especially for applications where its combination of insulating ability and high temperature strength enables it to perform as a "one shot" lining. It is a combination of calcined clays, lightweight aggregate, and improved calcium aluminate binder.

APPLICATIONS:

Fluid catalytic cracking units, naphtha reformers, coal gasifiers and other process furnaces requiring a semi-insulating, one shot lining.

CHEMICAL ANALYSIS - Calcined Basis

Silica ­ SiO2 Alumina ­ Al2O3 Iron Oxide ­ Fe2O3 Lime - CaO Magnesia - MgO Titania ­ TiO2 Alkalies ­ Na2O + K2O .................................................................................................. .................................................................................................. .................................................................................................. .................................................................................................. .................................................................................................. .................................................................................................. .................................................................................................. 45.0% 44.6% 1.1% 6.1% 0.3% 2.1% 0.8%

NOTE The test data shown are based on average results of control tests and are subject to normal variation on individual tests. These results cannot be taken as maximum or minimum requirements for specification purposes.

Ref: 212/5/9/08

KAST-O-LITE 26 LI C/G

PHYSICAL PROPERTIES

CAST DATA

MAXIMUM RECOMMENDED TEMPERATURE QUANTITY REQUIRED ­ Net BULK DENSITY Cured and Then Dried at 105°C PERMANENT LINEAR CHANGE ­ ASTM C113 AND C865 Expansion or Shrinkage Cured and Then Dried at 105°C Heated at 820°C and Then Cooled Heated at 1370°C and Then Cooled MODULUS OF RUPTURE ­ ASTM C133 AND C865 Cured and Then Dried at 105°C Heated at 820°C and Then Cooled Heated at 1095°C and Then Cooled COLD CRUSHING STRENGTH ­ ASTM C133 AND C865 Cured and Then Dried at 105°C Heated at 820°C and Then Cooled Heated at 1095°C and Then Cooled THERMAL CONDUCTIVITY at a Mean Temperature of 202°C 377°C 491°C 619°C 1427°C 1300 Kgs/m3 Kgs/m3 1300 - 1580

Nil 0.25% Shr 0.30% Shr MPa 1.0 - 5.0 0.5 - 3.0 0.5 - 3.0

2.0 - 6.0 2.0 - 6.0 1.0 - 3.0 W/mK 0.39 0.32 0.35 0.41

Ref: 212/5/9/08

Information

Microsoft Word - Kast-O-Lite 26 LI CG cast.doc