AISI 12L14 Steel, cold drawn, 19-38 mm round

COMPONENT WT. %

C Fe Mn P Pb S

PHYSICAL PROPERTIES METRIC

Max 0.15 97.91 - 98.7 0.85 - 1.15 0.04 - 0.09 0.15 - 0.35 0.26 - 0.35

ENGLISH COMMENTS

Density

MECHANICAL PROPERTIES

7.87 g/cc

METRIC

0.284 lb/in³

ENGLISH

Typical for steel

COMMENTS

Hardness, Brinell Hardness, Knoop Hardness, Rockwell B Hardness, Vickers Tensile Strength, Ultimate Tensile Strength, Yield Elongation at Break Reduction of Area Modulus of Elasticity Bulk Modulus Poisson's Ratio Machinability Shear Modulus

ELECTRICAL PROPERTIES

163 184 84 170 540 MPa 415 MPa 10% 35% 200 GPa 140 GPa 0.29 160% 80 GPa

METRIC

163 184 84 170 78300 psi 60200 psi 10% 35% 29000 ksi 20300 ksi 0.29 160% 11600 ksi

ENGLISH Typical for Steel Typical for Steel Typical for Steel Based on 100% machinability for AISI 1212 steel Typical for Steel Converted from Brinell hardness Converted from Brinell hardness Converted from Brinell hardness

COMMENTS

Electrical Resistivity

1.74e-005 ohm-cm

METRIC

1.74e-005 ohm-cm

ENGLISH

Typical for steel

THERMAL PROPERTIES

COMMENTS

CTE, linear 20°C CTE, linear 250°C CTE, linear 500°C CTE, linear 1000°C Specific Heat Capacity Thermal Conductivity

11.5 µm/m-°C 12.2 µm/m-°C 13.9 µm/m-°C 14.7 µm/m-°C 0.472 J/g-°C 51.9 W/m-K

6.39 µin/in-°F 6.78 µin/in-°F 7.72 µin/in-°F 8.17 µin/in-°F 0.113 BTU/lb-°F 360 BTU-in /hr-ft²-°F

Converted from Brinell hardness Converted from Brinell hardness Converted from Brinell hardness

AISI Type 303 Se Stainless Steel, cold drawn, bar, tested at RT

COMPONENT

WT. %

C Cr Fe Mn Ni P S Se Si

PHYSICAL PROPERTIES METRIC

Max 0.15 18 69 Max 2 9 Max 0.2 Max 0.06 Max 0.15 Max 1

ENGLISH COMMENTS

Density

MECHANICAL PROPERTIES

8 g/cc

METRIC

0.289 lb/in³

ENGLISH COMMENTS

Hardness, Brinell Hardness, Knoop Hardness, Rockwell B Hardness, Rockwell C Hardness, Vickers Tensile Strength, Ultimate Tensile Strength, Yield Elongation at Break Modulus of Elasticity Poisson's Ratio Shear Modulus

ELECTRICAL PROPERTIES

228 251 96 19 240 690 MPa 415 MPa 40% 193 GPa 0.25 77.2 GPa

METRIC

228 251 96 19 240 100000 psi 60200 psi 40% 28000 ksi 0.25 11200 ksi

ENGLISH COMMENTS at 0.2% offset in 50 mm tension Calculated Converted from Brinell hardness Converted from Brinell hardness Converted from Brinell hardness. Value below normal HRC range, for comparison only Converted from Brinell hardness

Electrical Resistivity

7.2e-005 ohm-cm

METRIC

7.2e-005 ohm-cm

ENGLISH COMMENTS

THERMAL PROPERTIES

CTE, linear 20°C CTE, linear 250°C CTE, linear 500°C Specific Heat Capacity Thermal Conductivity Melting Point Solidus Liquidus

17.2 µm/m-°C 17.8 µm/m-°C 18.4 µm/m-°C 0.5 J/g-°C 16.2 W/m-K 1400 - 1420 °C 1400 °C 1420 °C

9.56 µin/in-°F 9.89 µin/in-°F 10.2 µin/in-°F 0.12 BTU/lb-°F 112 BTU-in /hr-ft²-°F 2550 - 2590 °F 2550 °F 2590 °F

from 0-100°C at 0-315°C (32-600°F) at 0-540°C, 18.7 µm/m-C at 0-650°C from 0-100°C (32-212°F) at 100°C (212°F), 21.5 W/m-K at 500°C (930°F)

DISTRIBUTORS ­ INDIA NOBLE ENTERPRISES NOBLE FASTOTECH PVT. LTD

307 RAJA HOUSE , 30-31 NEHRU PLACE NEW DELHI ­ 110019 INDIA PHONES : +91-11-41617246 , +91-11-41617274 FAX : + 91-11-41617271 E-MAIL : [email protected]

MANUFACTURERS : E-ZLOK

240 E. Rosecrans Ave, Gardena, CA 90248

Information

3 pages

Find more like this

Report File (DMCA)

Our content is added by our users. We aim to remove reported files within 1 working day. Please use this link to notify us:

Report this file as copyright or inappropriate

303265